1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
L'adhesió del cinturó resistent a altes temperatures de tela de cotó és relativament baixa i l'adhesió del cinturó resistent a altes temperatures EP és relativament alta; La vida útil del cinturó resistent a altes temperatures EP és òbviament més llarga que la del cinturó resistent a altes temperatures de lona de cotó.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Aquest és un altre mètode d'enganxament, aquest mètode també és possible, però si feu servir aquest mètode, presteu atenció als punts següents:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Normalment, quan la temperatura de vulcanització és superior a la temperatura crítica de vulcanització de l'accelerador i l'agent de vulcanització i no pot arribar a la temperatura de vulcanització normal, es pot adoptar el mètode per allargar el temps de vulcanització per fer que la vulcanització del cautxú compleixi els requisits. En general, cada vegada que la temperatura és inferior a 10 graus, el temps de vulcanització s'allarga 2-4 vegades. Per descomptat, per raons de rendiment, no recomanem l'ús de vulcanització a baixa-temperatura i a llarg termini.
5. Can core rubbers from different manufacturers be mixed?
No es recomana barrejar el nucli de cautxú de diferents fabricants perquè la fórmula del nucli de cautxú de diferents fabricants és diferent. Hi ha molts tipus d'agents de composició al cautxú, i alguns d'ells tenen reaccions interactives. A la fórmula del mateix fabricant, no hi haurà agents de composició amb reaccions interactives adverses, però les fórmules de diferents fabricants són molt diferents. Quan s'utilitza, hi pot haver reflexos interactius dels agents de compostos, que afectaran l'efecte d'ús del nucli de cautxú.